110℃ High-shrink-ratio Polyolefin Tubing
|
|
MATERIAL：Polyolefin， Shrink ratio: 3:1。 600V
Operating temperature： -55 ℃ ~125 ℃ , Minimum shrink temperature : 70 ℃ ;
Minimum fully recovery temperature : 110 ℃ ,
COLOR:BLACK--BK、RED--RD、BLUE--BL、YELLOE-Y、WHITE--W、GREEN--G,
Other colors on Requrest.
Features：flame-retardant, high-shrink-ratio irradiated crosslinking heat-shrinkable modified polyolefin tubing.
Application：It is used for insulation protection, bundling or capsule of wire terminals and components with larger size differences.
Unit:mm |
|
|
|
|
Part No.
|
As supplied
|
After recovery
|
L
|
|
ID
|
T
|
（max.） ID
|
T
|
(m/spool)
|
|
UHS-110-3X-0.5-BK
|
1.8±0.2
|
0.20±0.05
|
0.5
|
0.50±0.10
|
200
|
|
UHS-110-3X-1-BK
|
3.3±0.3
|
1
|
0.60±0.10
|
|
UHS-110-3X-2-BK
|
6.5±0.3
|
2
|
0.70±0.10
|
100
|
|
UHS-110-3X-3-BK
|
9.5±0.4
|
0.30±0.06
|
3
|
0.80±0.15
|
|
UHS-110-3X-4-BK
|
12.5±0.4
|
4
|
0.85±0.15
|
|
UHS-110-3X-6-BK
|
18.5±0.5
|
6
|
1.00±0.150
|
50
|
|
UHS-110-3X-8-BK
|
26.0±1.0
|
0.40±0.10
|
8
|
1.20±0.20
|
|
UHS-110-3X-13-BK
|
41.5±1.0
|
13
|
1.20±0.20
|
|
|
Property
|
|
Chemical
|
Test method
|
Typical data
|
|
Physical
|
|
5% max.
|
ASTMD2671
|
≤5%
|
|
Concentricity
|
70% min.
|
ASTMD2671
|
≥70%
|
|
Tensile strength
|
10.4MPa min.
|
ASTMD638
|
≥14.0MPa
|
|
Elongation
|
200% min
|
ASTMD638
|
≥400%
|
|
|
No cracking
|
ASTMD2671
|
Pass
|
Low temperature flexibility
-55℃, 4hrs
|
No cracking
|
ASTMD2671
|
Pass
|
|
Aging 158℃,168hrs
|
|
Tensile strength after aging
|
70% of original min.
|
ASTMD638
|
≥90%
|
|
Elongation after aging
|
100% min.
|
ASTMD638
|
≥300%
|
|
Electrical
|
Dielectric voltage withstand
|
2500V,60sec,no breakdown
|
UL224
|
Pass
|
|
|
19.7KV㎜ min.
|
ASTMD2671
|
25KV/mm
|
|
|
1014Ω·㎝ min.
|
ASTMD876
|
≥1014Ω·㎝
|
|
Chemical
|
Corrosion
|
No corrosion
|
ASTMD2671
|
Pass
|
|
|
Elongation ≥100%
|
ASTMD2671
|
Pass
|
|
Flammability
|
VW﹣1
|
UL224
|
Pass
|
|